Product |
Low alumina mullite refractory castables (provincial new product) |
Mullite high strength refractory castables |
Mullite abrasion-resistant refractory castables |
||
Brand |
JC-M45 |
JC-M60 |
JC-M65 |
JC-M70 |
|
Maximum service temperature |
1400 |
1550 |
1600 |
1650 |
|
Bulk density (kg/m3)
|
110?漯span>×24h≥ |
220 |
2500 |
2600 |
2700 |
Chemical composition(%) |
Al2O3≥ |
45 |
60 |
65 |
70 |
SiO2+Al2O3≥ |
88 |
88 |
88 |
88(SiC) |
|
Cold modulus of
ruptuer(MPa)
|
110?漯span>×24h≥ |
8 |
10 |
11 |
11 |
1100?漯span>×3h≥ |
8 |
11 |
12 |
12 |
|
1500?漯span>×3h≥ |
?M |
?M |
?M |
12 |
|
Cold crushing
strength(MPa)
|
110?漯span>×24h≥ |
80 |
100 |
100 |
110 |
1100?漯span>×3h≥ |
80 |
110 |
120 |
120 |
|
1500?漯span>×3h≥ |
?M |
?M |
?M |
130 |
|
Linear change after
heating(%)
|
1100?榴imes;3h≤ |
-0.5 |
-0.5 |
-0.5 |
-0.5 |
1350?榴imes;3h≤ |
?M |
?M |
?M |
-0.5 |
|
Reference water addition for construction (%) |
6~7 |
6~7 |
6~7 |
6~7 |
|
Construction method |
Vibration |
||||
Service area |
Preheater system in large scale dry cement kilns |
Areas of high temperature and serious abrasion such sa back kiln mouth,kiln door hood,cooler short wall,etc. |
|||
Properties |
It has high strength and good alkali resistance,and was considered as an ideal alternative to -13NL,and has longer campaign life. |
After service,the surface was smooth and no crack is existed;it has better high temperature resistance. |
|||
Refractory steel fiber can be added as request and "teel fiber reinforced" should be added in front of the product name and an "F" shall be added behind the brand .The brand should be JC-M45F??JC-M60F??JC-M65F and JC-M70F. |